Table T7. X-ray fluorescence analysis on bulk powder samples from Hole C0002M.
|
Core, section |
Top depth (mbsf) |
Na2O (wt%) |
MgO (wt%) |
Al2O3 (wt%) |
SiO2 (wt%) |
P2O5 (wt%) |
K2O (wt%) |
CaO (wt%) |
TiO2 (wt%) |
MnO (wt%) |
Fe2O3 (wt%) |
Loss on ignition (wt%) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 348-C0002M- | ||||||||||||
| 1R-1 | 475.84 | 2.430 | 1.955 | 16.336 | 66.253 | 0.095 | 3.069 | 3.401 | 0.713 | 0.075 | 5.272 | 6.878 |
| 1R-2 | 477.04 | 2.525 | 1.897 | 15.993 | 65.962 | 0.095 | 3.085 | 3.629 | 0.688 | 0.066 | 5.034 | 6.711 |
| 1R-3 | 478.70 | 2.338 | 2.481 | 16.109 | 59.693 | 0.207 | 3.038 | 7.811 | 0.686 | 0.083 | 6.756 | 10.578 |
| 2R-2 | 486.98 | 2.555 | 1.833 | 14.877 | 69.985 | 0.081 | 2.92 | 2.766 | 0.621 | 0.064 | 5.057 | 5.367 |
| 2R-3 | 487.97 | 2.409 | 2.763 | 17.322 | 63.94 | 0.095 | 3.19 | 2.183 | 0.807 | 0.097 | 6.733 | 6.511 |
| 3R-1 | 494.32 | 2.395 | 2.017 | 16.638 | 65.604 | 0.103 | 3.156 | 2.614 | 0.719 | 0.068 | 5.667 | 6.704 |
| 3R-1 | 494.35 | 2.256 | 2.473 | 18.063 | 62.252 | 0.113 | 3.361 | 3.019 | 0.767 | 0.082 | 6.964 | 7.723 |
| 3R-2 | 495.09 | 2.212 | 2.664 | 17.938 | 60.609 | 0.18 | 3.383 | 3.405 | 0.767 | 0.104 | 8.112 | 8.59 |
| 4R-2 | 504.83 | 2.346 | 2.588 | 17.451 | 61.555 | 0.124 | 3.258 | 3.971 | 0.736 | 0.08 | 7.44 | 8.483 |
| 4R-2 | 505.51 | 2.313 | 2.731 | 17.325 | 60.127 | 0.131 | 3.231 | 4.9 | 0.764 | 0.094 | 7.647 | 9.208 |
| 4R-3 | 506.48 | 2.243 | 1.909 | 14.186 | 63.915 | 0.263 | 2.781 | 7.432 | 0.608 | 0.077 | 5.619 | 9.004 |
| Average: | 2.366 | 2.301 | 16.567 | 63.627 | 0.135 | 3.134 | 4.103 | 0.716 | 0.081 | 6.391 | 7.796 | |