Table T3. Hysteresis parameters for samples from Hole U1350A.

Core, section,
interval (cm)

Mr/Ms Hc (mT) Hcr (mT) Hcr/Hc
324-U1350A-
7R-1, 104−106 0.135 4.91 8.95 1.82
8R-1, 63−65 0.137 4.82 8.83 1.83
8R-2, 4−6 0.208 7.43 11.76 1.58
8R-3, 4−6 0.179 5.25 8.29 1.58
9R-1, 58−60 0.162 4.75 7.71 1.62
9R-5, 9−11 0.138 4.71 8.02 1.70
11R-1, 128−130 0.223 6.15 9.01 1.46
11R-2, 14−16 0.131 4.16 7.09 1.70
13R-1, 100−102 0.212 5.86 9.01 1.54
13R-2, 55−57 0.180 4.87 7.55 1.55
14R-1, 52−54 0.203 5.35 8.04 1.50
15R-1, 101−103 0.135 3.74 6.50 1.74
16R-2, 5−7 0.227 7.43 11.26 1.52
16R-3, 105−107 0.192 6.21 9.89 1.59
17R-1, 138−140 0.160 5.56 9.52 1.71
18R-1, 72−74 0.217 5.60 8.08 1.44
18R-2, 73−75 0.156 5.23 8.48 1.62
19R-1, 119−121 0.212 7.27 11.34 1.56
19R-2, 125−127 0.149 4.41 7.43 1.68
20R-1, 65−67 0.222 6.35 9.49 1.50
20R-1, 95−97 0.249 6.41 8.98 1.40
20R-2, 67−69 0.136 4.34 7.45 1.72
20R-2, 132−134 0.197 5.38 8.18 1.52
21R-1, 23−25 0.168 5.34 8.55 1.60
21R-1, 137−139 0.220 6.37 9.28 1.46
21R-2, 135−137 0.309 9.20 12.33 1.34
21R-3, 64−66 0.193 6.02 9.56 1.59
22R-2, 67−69 0.229 6.44 9.29 1.44
22R-2, 68−70 0.280 8.81 13.56 1.54
22R-4, 87−89 0.225 7.13 11.49 1.61
22R-5, 71−73 0.176 6.07 10.40 1.71
22R-5, 135−137 0.213 7.55 13.09 1.73
23R-1, 22−24 0.152 5.58 10.33 1.85
23R-3, 125−127 0.166 5.76 10.22 1.78
23R-4, 16−18 0.268 9.57 15.40 1.61
23R-5, 6−8 0.381 21.64 32.97 1.52
24R-1, 42−44 0.275 10.15 16.21 1.60
24R-1, 111−113 0.263 12.56 21.85 1.74
24R-2, 137−139 0.281 10.26 16.44 1.60
24R-3, 27−29 0.222 8.15 13.61 1.67
25R-1, 61−63 0.218 7.56 12.32 1.63
25R-1, 102−104 0.267 7.47 10.94 1.47
25R-1, 112−114 0.257 7.59 11.05 1.46
25R-2, 60−62 0.311 9.68 13.39 1.38
25R-2, 64−66 0.253 9.21 15.01 1.63
25R-3, 80−82 0.245 8.96 13.71 1.53
25R-3, 83−85 0.281 8.02 11.54 1.44
25R-5, 92−94 0.256 7.29 10.70 1.47
25R-6, 31−33 0.284 8.26 11.94 1.44
25R-7, 5−7 0.235 7.83 13.39 1.71
25R-7, 91−93 0.284 7.97 11.29 1.42
25R-8, 13−15 0.372 14.21 19.52 1.37
26R-1, 28−30 0.295 10.02 14.81 1.48
26R-2, 12−14 0.254 9.35 14.96 1.60
26R-2, 40−42 0.277 7.86 11.15 1.42
26R-3, 6−8 0.276 9.44 14.44 1.53
26R-4, 39−41 0.194 6.00 10.20 1.70
26R-4, 89−91 0.173 6.83 12.91 1.89
26R-6, 12−14 0.252 7.02 10.42 1.48
26R-6, 80−82 0.198 7.09 12.41 1.75
26R-7, 13−15 0.260 7.12 10.18 1.43
26R-7, 9−11 0.189 6.00 13.00 2.17
26R-7, 96−98 0.241 9.62 15.78 1.64
26R-8, 43−45 0.259 7.61 11.05 1.45

Mr = remanent magnetization, Ms = saturation magnetization, Hc = coercive field, Hcr = remanent coercivity field. Parameters from Carvallo and Camps (2013) are included.