Table T7. ICP-AES analyses, Hole U1362A. (See table notes.) (Continued on next two pages.)

Hole:
327-U1362A-
Core, section:
2R-1 2R-2 3R-1 3R-2 4R-1 5R-1 5R-2 6R-1 7R-1 8R-1 8R-2 8R-2
Interval (cm):
92–94 73–83 95–99 127–130 26–29 147–149 58–61 128–131 6–8 113–117 100–102 126–128
Unit/Subunit:
1A 1A 1A 1A 1A 1B 1B 1B 1B 2 2 2
Depth (mbsf):
346.93 348.28 353.57 355.355 362.475 366.18 366.795 371.495 379.87 390.65 391.98 392.24
Sample:
WDGE 2390221 WDGE 2390231 WDGE 2390251 WDGE 2390271 WDGE 2390321 WDGE 2390351 WDGE 2392651 WDGE 2392701 WDGE 2395851 WDGE 2395901 WDGE 2395951 WDGE 2395971
Major element oxide (wt%):
SiO2 49.46 49.49 48.73 49.72 48.18 49.69 47.90 50.97 50.03 49.44 49.90 49.88
Al2O3 14.85 15.00 14.68 15.61 15.27 15.40 14.68 15.59 16.14 15.38 15.31 15.48
Fe2O3 10.39 9.21 10.00 10.81 9.91 9.18 10.57 10.04 9.78 10.44 10.51 10.13
MnO 0.17 0.16 0.17 0.17 0.17 0.16 0.17 0.16 0.17 0.17 0.18 0.15
MgO 7.53 7.76 7.54 7.73 7.43 7.83 7.57 8.19 7.61 7.40 7.49 7.90
CaO 11.79 11.55 11.60 12.37 11.71 11.75 11.94 12.24 12.27 11.64 11.99 11.89
Na2O 2.75 2.84 2.60 2.70 2.65 2.72 2.59 2.74 2.67 2.84 2.79 2.90
K2O 0.20 0.10 0.14 0.23 0.26 0.12 0.28 0.13 0.11 0.11 0.13 0.07
TiO2 1.66 1.68 1.44 1.50 1.48 1.50 1.47 1.52 1.46 1.80 1.77 1.78
P2O5 0.13 0.13 0.11 0.12 0.11 0.11 0.09 0.11 0.11 0.12 0.12 0.12
Totals:
98.95 97.92 97.02 100.96 97.17 98.46 97.27 101.69 100.35 99.34 100.18 100.31
Trace element (ppm):
Ba 16 17 16 12 15 16 17 17 12 11 13 17
Co 55 60 53 54 59 77 56 54 55 73 60 55
Cr 171 153 140 176 155 157 162 166 129 132 132 129
Cu 87 79 77 93 87 99 77 88 84 59 64 76
Ni 57 96 73 64 97 112 70 73 87 98 70 68
Sc 48 47 44 47 47 47 45 48 44 50 50 51
Sr 127 127 111 116 115 117 111 117 117 120 119 122
V 326 343 312 327 326 332 316 328 323 374 367 372
Zn 93 93 88 90 91 91 91 91 90 76 95 98
Zr 104 107 89 93 89 92 89 93 89 112 109 109
LOI (wt%) 0.72 0.83 0.63 0.64 1.11 0.53 0.69 0.75 0.99 1.22 1.24 1.07
Mg# 61.47 64.96 62.42 61.15 62.28 65.25 61.21 64.22 63.15 60.94 61.06 63.19

Notes: ICP-AES = inductively coupled plasma–atomic emission spectroscopy. LOI = loss on ignition. Mg# = (MgO/40.305)/[(MgO/40.305) + 0.9 × 2 × (Fe2O3/159.694)] × 100.